Deterioration of Shirahama Sandstone in Fatigue Failure Process.

DOI Web Site 1 Citations 17 References

Bibliographic Information

Other Title
  • 疲労破壊過程における白浜砂岩の劣化
  • ヒロウ ハカイ カテイ ニ オケル シラハマ サガン ノ レッカ

Search this article

Abstract

In order to clarify the fatigue failure process of shirahama sandstone, fatigue tests were done, and deformation characteristics and AE occurrence behavior were investigated. Then, the strength of specimens, which loading and unloading were repeatedly applied to for some times, and crack development in them were examined.<BR>In the fatigue test, fatigue failure occurs in the comparatively short time (about 3.5 days), when upper limit stress corresponds to the stress at stage C of uniaxial compression failure process, where the volume of the rock specimen expands. The fatigue failure process are divided into three stage (I, II, III) from change in strain and AE activity. Lowering the strength of the rock specimen begins from stage II of fatigue failure process, and it is in a good correlation with the increase in lateral / axial strain ratio. The value of b obtained from the relationship between AE event frequency and AE energy of each event decreases when macroscopic cracks develop in the specimen.

Journal

  • Shigen-to-Sozai

    Shigen-to-Sozai 117 (9), 711-717, 2001

    The Mining and Materials Processing Institute of Japan

Citations (1)*help

See more

References(17)*help

See more

Keywords

Details 詳細情報について

Report a problem

Back to top