G0601-7-6 Thermal Decomposition Behavior of Plastics with Flame Retardant under Constant Temperature Condition
-
- KURIHARA Takurou
- Gunma University
-
- YAMAMOTO Yasuo
- Komatsu Co., Ltd
-
- FURUHATA Tomohiko
- Gunma University
-
- ARAI Masataka
- Gunma University
-
- SAITOU Masahiro
- Gunma University
Bibliographic Information
- Other Title
-
- G0601-7-6 一定温度条件下におけるプラスチックの熱分解特性におよぼす難燃剤の影響(熱工学(7)燃焼(2))
Abstract
In order to develop effective final treatment system of waste plastics, thermal gasification characteristics of plastics compounds containing flame retardant were investigated. Polypropylenes (PP) which contained Al(OH)_3 or (NH_4PO_3)_n as a flame retardant were decomposed and burned under constant temperature condition in an image furnace while changing O_2 concentration from 0% to 21%. Mass reduction during thermal decomposition was measured by an electric-micro balance. The gas components produced by the thermal decomposition and combustion process were analyzed with a gas analyzer. It was found that HC concentration for PP was the highest at 10% oxygen concentration when the ambient temperature Τ_a was 1073K. CO_2 concentration for PP contained 20wt% Al(OH)_3 was higher than PP under 21% oxygen concentration.
Journal
-
- The proceedings of the JSME annual meeting
-
The proceedings of the JSME annual meeting 2009.3 (0), 77-78, 2009
The Japan Society of Mechanical Engineers
- Tweet
Details 詳細情報について
-
- CRID
- 1390001206063445504
-
- NII Article ID
- 110007861728
-
- ISSN
- 24331325
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed