High Dielectric Constant Negative-Positive-Zero Dielectric Materials Based on (100-x)(La<sub>0.1</sub>Bi<sub>0.9</sub>)Ti<sub>2</sub>O<sub>7-x</sub>SrTiO<sub>3</sub>
-
- Nakano Atsuyuki
- TDK Corporation, Materials Research Center, Narita, Chiba 286, Japan
-
- Cann David P.
- Materials Research Laboratory, The Pennsylvania State University, University Park, PA 16802, USA
-
- Shrout Thomas R.
- Materials Research Laboratory, The Pennsylvania State University, University Park, PA 16802, USA
書誌事項
- タイトル別名
-
- High Dielectric Constant Negative-Positive-Zero Dielectric Materials Based on (100-x)(La0.1Bi0.9)Ti2O7-xSrTiO3.
- High Dielectric Constant Negative Posit
この論文をさがす
抄録
Dielectric materials based on the solid solution system (100-x)( La0.1Bi0.9) Ti2O7-xSrTiO3 have been studied in order to obtain high performance capacitor materials. Compositions with temperature coefficient of capacitance as low as τ c<20 ppm and dielectric constant as high as 250 make them suitable for negative-positive-zero (NPO) capacitor designated applications. Using X-ray diffraction, a three-phase mixture of the two end members, SrTiO3, ( La0.1Bi0.9) Ti2O7, and a Bismuth-layer structure phase with only a limited amount of solid solution was observed. The low-temperature coefficient of capacitance was believed to be the result of the balancing of the positive and negative temperature coefficients characteristic of the three constituent phases.
収録刊行物
-
- Japanese Journal of Applied Physics
-
Japanese Journal of Applied Physics 36 (3A), 1136-1140, 1997
The Japan Society of Applied Physics
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206247961728
-
- NII論文ID
- 210000040726
- 110003905722
- 130004523382
-
- NII書誌ID
- AA10457675
-
- ISSN
- 13474065
- 00214922
-
- NDL書誌ID
- 4187856
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可