Corrosion Behavior of Prestressing Steel in a Solution of 20% Ammonium Thiocyanate
-
- Ichiba Mikiyuki
- R&D Center, Tokyo Electric Power Company
-
- Niidome Yuya
- R&D Center, Tokyo Electric Power Company
-
- Nakamura Shunsuke
- School of Science and Engineering, Waseda University (Present: Komatsu Ltd.)
-
- Sakai Junʼichi
- Faculty of Science and Engineering, Waseda University
Bibliographic Information
- Other Title
-
- チオシアン酸アンモニウム溶液中のPC鋼材の腐食挙動
- チオシアンサン アンモニウム ヨウエキ チュウ ノ PC コウザイ ノ フショク キョドウ
Search this article
Abstract
High-strength steels or PC steel products are used for pre-stressed concrete structures. Testing of PC steel products in terms of hydrogen embrittlement is specified in the FIP Report, and the test method adopted in ISO 15630 is well known. This test is called the FIP test, whereby a constant load is applied to PC steel in a 20%, 50℃ ammonium thiocyanate solution. An investigation was carried out on the corrosion behavior of 1,400 MPa class PC steel products in a FIP testing environment. Under this testing environment, a cathodic reaction associated with oxygen consumption and hydrogen generation was identified from the initial stage of dipping, and corrosive products mainly consisting of ferric sulfide were formed on the surface of a specimen detected in the test pieces. From changes in the amount of gas associated with the reaction, it is understood that, together with this corrosion reaction, there also occurred a reaction involving 1 mol of hydrogen generation or 0.5 mol of oxygen consumption for 1 mol dissolution of iron. It is also assumed that the reaction involving hydrogen generation was a cathodic reaction associated with the decomposition of SCN-.
Journal
-
- Zairyo-to-Kankyo
-
Zairyo-to-Kankyo 62 (8), 289-293, 2013
Japan Society of Corrosion Engineering
- Tweet
Details 詳細情報について
-
- CRID
- 1390001206258125952
-
- NII Article ID
- 10031190994
-
- NII Book ID
- AN10235427
-
- COI
- 1:CAS:528:DC%2BC3sXhs1ahtbbF
-
- ISSN
- 18819664
- 09170480
-
- NDL BIB ID
- 024844709
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed