Sulfidation Behavior of Preoxidized Fe-13Cr and Fe-18Cr-3Al Alloys in H<sub>2</sub>S-H<sub>2</sub> Atmosphere
-
- Nakamori Masaharu
- Takasago Research & Development, Mitsubishi Heavy Industries, LTD
-
- Mizuta Ikuji
- Takasago Research & Development, Mitsubishi Heavy Industries, LTD
-
- Ishikawa Tatsuo
- Faculty of Engineering, Hokkaido University
-
- Narita Toshio
- Faculty of Engineering, Hokkaido University
Bibliographic Information
- Other Title
-
- 予備酸化したFe-13CrおよびFe-18Cr-3Al合金の高温硫化腐食挙動
- ヨビ サンカシタ Fe 13Cr オヨビ Fe 18Cr 3Al ゴウキン ノ
Search this article
Abstract
The sulfidation behavior was investigated of two kinds of the preoxidized Fe-13Cr and Fe-18Cr-3Al alloys for the water wall tubes in oil firing boilers. A McBain balance assembly and CCD sensor were used to determine a sulfidation rate in 1.92% H2S-H2 atmosphere. The oxide scale formed on the preoxidized Fe-13Cr alloy was effective to prevent the sulfidation attack at 973K, although it was hardly effective above 873K. On the other hand, the oxide scale on Fe-18Cr-3Al alloy showed remarkable retardation effect on the sulfidation attack at 973K to 1073K. It is concluded that the difference of sulfidation behavior of those preoxidized alloys is attributed to the difference of the scale formation mechanism. The scale on the Fe-13Cr alloy was composed of Cr2O3 and Fe2O3 which was subsequently sulfidized. On the contrary the scale on the Fe-18Cr-3Al alloy was formed mainly with fine Cr2O3 layer which is capable to prevent the sulfidation attack.
Journal
-
- CORROSION ENGINEERING
-
CORROSION ENGINEERING 39 (11), 597-602, 1990
Japan Society of Corrosion Engineering
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390001206258844288
-
- NII Article ID
- 130004732145
- 130006025365
-
- NII Book ID
- AN00225595
-
- ISSN
- 18841155
- 00109355
-
- NDL BIB ID
- 3694363
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed