Corrosion Resistance and Biocompatibility of High Nitrogen-bearing Stainless Steels
-
- Endo Kazuhiko
- Department of Dental Materials Science, School of Dentistry, Health Sciences University of Hokkaido
-
- Abiko Yoshihiro
- Department of Oral Pathology, School of Dentistry, Health Sciences University of Hokkaido
-
- Suzuki Masahiro
- Department of Dental Materials Science, School of Dentistry, Health Sciences University of Hokkaido
-
- Ohno Hiroki
- Department of Dental Materials Science, School of Dentistry, Health Sciences University of Hokkaido
-
- Kaku Tohru
- Department of Oral Pathology, School of Dentistry, Health Sciences University of Hokkaido
書誌事項
- タイトル別名
-
- Corrosion Resistance and Biocompatibili
この論文をさがす
抄録
The corrosion resistance and cytocompatibility of two high N-bearing austenitic stainless steels as well as SUS 316L were evaluated in a simulated physiological environment. Potentiodynamic polarization measurements and analysis of released metal ions from alloy specimens immersed in 0.9% NaCl solution were made to evaluate the corrosion resistance. The surface of the alloys was characterized with X-ray photoelectron spectroscopy (XPS). Cell growth of human gingival fibroblasts was examined under culture conditions on these alloy surfaces. The pitting potential of the high N-bearing Fe-Cr-Mn-Mo alloy was higher than that of high N-bearing Fe-Cr-Mn alloy and SUS 316L. CrN formed in the outer region of the passive film and N enriched at the alloy surface under the passive film may be effective in improving pitting corrosion resistance. The present study demonstrated a correlation between corrosion resistance and metal-induced cytotoxity. The amount of released Fe and Cr ions from high N-bearing Fe-Cr-Mn alloy was approximately one order of magnitude higher than that from high N-bearing Fe-Cr-Mn-Mo alloy and SUS 316L. The cell growth rate on the high N-bearing Fe-Cr-Mn alloy was markedly depressed because of the large amount of released metal ions. The characteristics of the high N-bearing Fe-Cr-Mn-Mo austenitic stainless steel such as non-magnetism, high localized corrosion resistance, and excellent cytocompatibility meet the requirements for use as an implant material.
収録刊行物
-
- Zairyo‐to‐Kankyo
-
Zairyo‐to‐Kankyo 47 (9), 570-576, 1998
公益社団法人 腐食防食学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206259165440
-
- NII論文ID
- 130004238600
- 10002174939
-
- NII書誌ID
- AN10235427
-
- COI
- 1:CAS:528:DyaK1cXmt1Wlsbw%3D
-
- ISSN
- 18819664
- 09170480
- http://id.crossref.org/issn/05145163
- http://id.crossref.org/issn/09170480
-
- NDL書誌ID
- 4559392
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可