Stress Corrosion Cracking in Hot Water Tank of Type 304 Steel caused from a Weld Defect
-
- Tsutsui Mitsunori
- Nagoya Municipal Industrial Research Institute
-
- Yamada Takashi
- Nagoya Municipal Industrial Research Institute
Bibliographic Information
- Other Title
-
- 溶接不良によるステンレス製給湯タンクの腐食割れ
- ヨウセツ フリョウ ニ ヨル ステンレスセイ キュウトウ タンク ノ フショク
Search this article
Description
Stress corrosion cracking was found in Type 304 steel tank for hot water with Cl- content of 19ppm and temperature of 80°C. It was learned that poor penetration in butt welding left a gap of 40μm in the tank wall, which would behave as a corrosion crevice to initiate cracks under residual stresses.
Journal
-
- CORROSION ENGINEERING
-
CORROSION ENGINEERING 35 (9), 521-523, 1986
Japan Society of Corrosion Engineering
- Tweet
Details 詳細情報について
-
- CRID
- 1390001206259442560
-
- NII Article ID
- 130006025100
- 130004731880
-
- NII Book ID
- AN00225595
-
- ISSN
- 18841155
- 00109355
- http://id.crossref.org/issn/00109355
-
- NDL BIB ID
- 3095941
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed