- Corrosion Inhibition of Carbon Steel by Ruthenium Salt in Concentrated Lithium Bromide Solution at Elevated Temperature
- コウオン ノウコウ シュウカ リチウム スイヨウエキチュウ ニ オケル ルテニ
この論文をさがす
抄録
Corrosion inhibition of carbon steel by metal salts in 12.5mol/dm3 LiBr solution, which is used as a practical absorbent in an absorption refrigeration system at the highest temperature of 433K, was studied. Among salts of iron, cobalt, nickel, ruthenium, rhodium, palladium, platinum and copper examined, ruthenium salt was the most effective inhibitor on carbon steel in the presence of LiOH. The best inhibition effect of ruthenium salt and LiOH was obtained at respective concentration of 8×10-4 and 0.15mol/dm3. In this case, conversion of Fe (II) to magnetite was accelerated by the inhibitor and a dense protective film was formed on carbon steel.
収録刊行物
-
- CORROSION ENGINEERING
-
CORROSION ENGINEERING 35 (8), 455-461, 1986
社団法人 腐食防食協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206259453952
-
- NII論文ID
- 130004731873
- 130006025017
-
- NII書誌ID
- AN00225595
-
- ISSN
- 18841155
- 00109355
- http://id.crossref.org/issn/00109355
-
- NDL書誌ID
- 3095886
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可