Synthesis and Characterization of Novel Aromatic Polyimides from Aromatic Diamine and 3,3′′′′′,4,4′′′′′-p-Sexiphenyltetracarboxylic Dianhydride
-
- MORIKAWA Atsushi
- Department of Materials Science, Faculty of Engineering, Ibaraki University, 4-12-1 Nakanarusawa, Hitachi, Ibaraki, 316-8511, Japan
-
- ONO Katsumichi
- Department of Materials Science, Faculty of Engineering, Ibaraki University, 4-12-1 Nakanarusawa, Hitachi, Ibaraki, 316-8511, Japan
書誌事項
- タイトル別名
-
- Synthesis and Characterization of Novel Aromatic Polyimides from Aromatic Diamine and 3,3''''',4,4'''''-p-Sexiphenyltetracarboxylic Dianhydride.
この論文をさがす
抄録
A new rigid tetracarboxylic dianhydride, 3, 3''''', 4, 4'''''-p-sexiphenyltetracarboxylic dianhydride, was synthesized in seven steps starting from diethyl 4-bromophthalate. New aromatic polyimides containing a p-sexiphenyl unit were synthesized from this tetracarboxylic dianhydride and various aromatic diamines by the conventional two-step procedure of ring-opening polyaddition in a polar amide-type solvent and subsequent thermal cyclic dehydration. These polyimides had inherent viscosities of 1.20—1.69dLg-1, and were insoluble in organic solvents. The polyimides were characterized by differential scanning calorimetry (DSC), thermogravimetry (TG), wide-angle X-Ray diffraction measurements, and dynamic mechanical analysis (DMA). Typical polyimides were noncrystalline and showed excellent thermal stability, and had glass transition temperatures (Tg) at about 250°C. Decrease in the modulus at the glass transition temperature was less than corresponding polyimides having no p-sexiphenyl unit due to the presence of the rigid p-sexiphenyl unit.
収録刊行物
-
- Polymer Journal
-
Polymer Journal 32 (11), 948-953, 2000
The Society of Polymer Science, Japan
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206287770880
-
- NII論文ID
- 130004430133
- 10006262272
-
- NII書誌ID
- AA00777013
-
- COI
- 1:CAS:528:DC%2BD3cXot1Gksb4%3D
-
- ISSN
- 13490540
- 00323896
-
- NDL書誌ID
- 5570710
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可