Poly(3-phenylgalvinoxylthiophene). A New Conjugated Polyradical with High Spin Concentration.
-
- Miyasaka Makoto
- Department of Applied Chemistry, Waseda University
-
- Yamazaki Tomoko
- Department of Applied Chemistry, Waseda University
-
- Nishide Hiroyuki
- Department of Applied Chemistry, Waseda University
この論文をさがす
抄録
3-{4-[(3,5-Di-tert-butyl-4-acetoxyphenyl)(3,5-di-tert-butyl-4-oxocyclohexa-2,5-diene-1-ylidene)methyl]phenyl} thiophene (2a) was synthesized and oxidatively polymerized with ferric chloride at low temperature to yield poly(3-{4-[(3,5-di-tert-butyl-4-acetoxyphenyl)(3,5-di-tert-butyl-4-oxocyclohexa-2,5-diene-1-ylidene)methyl]phenyl} thiophene) (1a). Head-to-tail content of 1a with a molecular weight of >104 reached 92%. This polymer has a quinoid chromophore, and it reversibly showed a dark blue and red brownish color ascribed to an anion and a radical form, respectively. The polyradical 1 was almost quantitatively generated from 1b (a spin concentration of 0.9 spin/galvinoxyl unit), which was persistent at room temperature. The SQUID measurement at low temperature gave a spin quantum number (S) of 1/2 for 1, which indicated a paramagnetic ground state. 1 doped with iodine showed an electrical conductivity of 10-5 S cm-1. The polyradical derivatives, 7 and 8, displayed S of 1/2–2/2 and 1/2, respectively, and an electrical conductivity of 10-4–10-3 S cm-1 after doping.
収録刊行物
-
- Polymer Journal
-
Polymer Journal 33 (11), 849-856, 2001
The Society of Polymer Science, Japan
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206289098752
-
- NII論文ID
- 130004430272
- 10010078139
-
- NII書誌ID
- AA00777013
-
- COI
- 1:CAS:528:DC%2BD3MXos1OhtLY%3D
-
- ISSN
- 13490540
- 00323896
-
- NDL書誌ID
- 5985216
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可