- MOYSÉS Sílvio CALAFATI
- Department de Física, Universidade Federal do Paraná, Caixa Postal 19081, 81531-990 Curitiba (PR), Brazil
説明
On the bases of small-angle X-ray scattering (SAXS) and differential scanning calorimetry (DSC) techniques it is possible to show that low density polyethylene (LDPE) annealed at 40°C divides its original crystal population into two: the first one melts at the annealing temperature, recrystallize and continuously thicken to improve its stability. The fraction that does not melt at 40°C is unable to increase its lamellar thickness, although it shows crystal lateral growth. Finally, an interesting phenomenon was detected through the SAXS analysis: a transition of polymer segments from the interphase towards to the amorphous phase. This process occurs inside the stacks of the original crystals which remain unmelted at 40°C.
収録刊行物
-
- Polymer Journal
-
Polymer Journal 32 (6), 486-491, 2000
The Society of Polymer Science, Japan
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206290450816
-
- NII論文ID
- 130004430200
-
- COI
- 1:CAS:528:DC%2BD3cXktlWms7o%3D
-
- ISSN
- 13490540
- 00323896
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可