- Partial Oxidation of Methane to Synthesis Gas over (La,Sr)(Co,Ni) Oxide Catalysts.
- Partial Oxidation of Methane to Synthes
この論文をさがす
説明
The catalytic properties of a series of (La, Sr)(Co, Ni) oxides have been studied for the oxidation of CH4. The catalysts were prepared by the citrate method. The catalytic test using a mixed gas of CH4 and air was carried out by temperature programmed reaction (TPR) from room temperature to 800°C.<br>All the catalysts prepared possessed perovskite oxide structure. The mode of the catalytic oxidation substantially changed around 700°C during the TPR. The oxide catalysts generally catalyzed combustion or oxidative dimerization of CH4 at temperatures below 700°C, while some of the oxides, La1-xSrxNiO3-δ(0≤x≤0.1) and La2-xSrxNiO4-δ(0.1≤x≤1.0), catalyzed synthesis gas production from CH4 at temperatures above 700°C. The latter two oxide catalysts decomposed to form La2O3 and Ni metal after the reaction at 800°C, and the Ni metal seemed to be active species for the synthesis gas formation. However, significant coke formation was observed over the catalysts, resulting in a blockage in the reactor in a short time.<br>LaCoO3-δ was stable and active for the CH4 combustion during the TPR, and showed a very low activity for synthesis gas production at 800°C, where Co metal was not observed. Partial substitution of Sr for La and of Ni for Co, respectively, in LaCoO<sub>3-δ</sub>, i.e., La0.8Sr0.2Co0.8Ni0.2 mixed oxide, resulted in a stable activity for synthesis gas production. The activity was enhanced by pretreating the catalyst, i.e., the reduction with CH4.
収録刊行物
-
- 石油学会誌
-
石油学会誌 39 (5), 314-321, 1996
公益社団法人 石油学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206294412672
-
- NII論文ID
- 10003817357
-
- NII書誌ID
- AN00130954
-
- NDL書誌ID
- 4021153
-
- ISSN
- 05824664
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可