- 井上 明久
- 東北大学金属材料研究所
書誌事項
- タイトル別名
-
- Study on the Production of Amorphous Metallic Powders by Impact Flattening of Atomized Liquid Droplets on a Rapidly Rotating Wheel.
- カイテン エンスイタイ エ ノ ゴウキン エキテキ コウアツ ガス フキツケ
この論文をさがす
抄録
A two-stage quenching technique consisting of impact flattening of atomized supercooled liquid droplets caused the production of flaky amorphous powders with a thickness of 1 to 3 pm and an aspect ratio of 20 to 300 in Co-, Fe- and Al-based systems. The flaky powders consist of an amorphous phase over the entire particle size range even in the alloy systems where no amorphous phase is formed in the particle size below 25 μm by high-pressure gas atomization. The improvement of the production ratio of the amorphous powders is due to the following three factors; (1) the second-stage cooling of supercooled liquid droplets, (2) the reduction of powder thickness to 1 to 3 Jim, and (3) the high thermal conductive state between rotator and powder resulting from the high-energy collision. The flaky powders also have smooth surface and edge combined with a uniform thickness, leading to good luster, high reflection ratio against light, high corrosion resistance, high mechanical strength and anisotropic magnetic properties. Furthermore, the unique morphology causes a high laminating tendnency in a resin. By utilizing these advantages, the flaky amorphous powders are expected to be used as magnetic filler and corrosion-resistant coating materials.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 40 (3), 347-354, 1993
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206304030080
-
- NII論文ID
- 130000819222
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 3812484
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可