Influences of alloy elements in infiltrant on mechanical properties of copper-alloy infiltrated P/M high speed steels.

DOI Web Site 1 Citations

Bibliographic Information

Other Title
  • 銅溶浸焼結高速度鋼の諸性質に及ぼす溶浸材中の配合元素の影響
  • ドウ ヨウシン ショウケツ コウソクド コウ ノ ショ セイシツ ニ オヨボス

Search this article

Abstract

Elements in Infiltrant on Mechanical Properties of Copper-alloy Infiltrated P/M High Speed Steels<BR>Mechanical properties of copper-alloy infiltrated M42, T42 P/M high speed steels were studied.The green compacts were sintered in vacuum at 1433, 1443, 1453 K to make skeletons. The skeletons were infiltrated with Cu-Cr, Cu-Co and Cu-Fe-Mn alloy infiltrants in hydrogen or argon at 1423 K for 1.8 ks.The result obtained were summarized as follows.<BR>1)All the infiltrated specimens shrinked.The Cu-Fe-Mn infiltrated M42, T42 P/M high speed steels had the least amount of dimentional change values during infiltration.The Cu-Fe-Mn infiltrated M42, T42 P/M steels had comparatively high hardness, but low strength.<BR>2)Cu-Cr, Cu-Co infiltrated P/M high speed steels showed high strength, especially the P/M M42 steel having a skeleton sintered at 1453 k in vacuum and infiltrated with the Cu-Co alloy infiltrant in hydrogen had 2450 MPa of transverse rupture strength and HRC 48 of hardness as infiltrated.

Journal

Citations (1)*help

See more

Keywords

Details 詳細情報について

Report a problem

Back to top