ＭＡ‐ＰＳ（プラズマ加圧焼結）法による傾斜機能材料の創製

DOI Web Site 被引用文献2件

書誌事項

タイトル別名
  • Fabrication of Functionally Gradient Materials by a MA-PS (Plasma Sintering) Technique.
  • MA-PS プラズマ カアツ ショウケツ ホウ ニ ヨル ケイシャ キノウ ザ

この論文をさがす

抄録

A novel P/M processing is developed, which consists of plasma sintering with the aid of an applied stress and a temperature gradient and a high quality powder production of amorphous TiAI by mechanical alloying, for the fabrication of a functionally gradient materials(FGM) of zirconia-titanium aluminide system. Our processing makes it possible to obtain a FGM of FSZ/TiAl without a visible crack-like discontinuity throughout an overall cross section with a short-time sintering of 300 s and a relatively low applied stress ranging from 29 to 59 MPa. Plasma sintering leads to a full dense compaction, mainly via viscous flow in amorphous TiAl matrix, in layers between TiAI and 50%-TiAl/FSZ, and a relatively high hardness of 807 Hv for 7-phase TiAl including a small amount. of α2(Ti3Al) and at the maximum, 1016 Hv at 25 %FSZ/TiAl. These higher levels are explained by strengthening mechanisms of nano-meter scaled grain and FSZ particle dispersion respectively. Two-step plasma sintering with a greater temperature gradient realizes the enhanced hardness and relative density of FSZ-rich layers.

収録刊行物

被引用文献 (2)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ