- Effect of Li Addition to the Low-Tc Phase in the Bi-Sr-Ca-Cu-O System. (I).
- Bi Sr Ca Cu Oケイ テイオンソウ エ ノ Li テンカ コウカ 1
この論文をさがす
抄録
The effect of Li-addition to the low-Tc phase in Bi-Sr-Ca-Cu-O system have been studied for the samples with nominal compositions of Bi:Sr:Ca:Cu:Li=2:1.5:1.5:2-x:x heated at 720 to 845°C for 12 to 24h in air (x=0 to 0.8). The Li-addition promotes the formation of the low-Tc phase. Single phase of the low-Tc phase was obtained for the sample with x=0.2 to 0.4 more easily than the sample with x=0. The lattice constant c of the low-Tc phase increases as the Li content increases. As the heating period becomes longer, the amount of Li content in the low-Tc phase decreases.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 39 (9), 763-766, 1992
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206305616000
-
- NII論文ID
- 40003439353
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 3782629
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可