- 2相分離型Cu‐V系のN2雰囲気中のMAによるアモルファス化
- 2ソウ ブンリガタ Cu Vケイ ノ N2 フンイキチュウ ノ MA ニ ヨル
Search this article
Abstract
Mechanical aloying(MA) under the N2 gas atmosphere was capable of amorphizing V70Cu30 powders which is characterized by a positive heat of mixing (ΔHmix=5 kJ/mol). The S(Q) observed by X-ray diffraction gradually changed into the structure characteristic of an amorphous state with increasing milling time. The S(Q) observed by neutron diffraction after 200 hours of milling possesses a mixture of both amorphous and crystal phases. Since the coherent scattering length of the V atom in the neutron diffraction is negligibly small, small crystal peaks shoud be due the Cu crystal. The growth of a new peak at Q=4.25 A-1 in the S(Q) was observed after 40 and 120 hours of milling and then it disappeared after 200 hours of milling. This peak is attributable to the bcc Cu crystal formed by dissolving Cu atoms into the bcc V lattice. The results can be interpreted that the bcc solid solution is formed at the early stage of milling but becomes amorphized due to the gradual incorporation of N atoms in the subsequent stage of milling.
Journal
-
- Journal of the Japan Society of Powder and Powder Metallurgy
-
Journal of the Japan Society of Powder and Powder Metallurgy 40 (1), 92-95, 1993
Japan Society of Powder and Powder Metallurgy
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390001206306120704
-
- NII Article ID
- 130000818317
-
- NII Book ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL BIB ID
- 3812474
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed