- Preparation and Magnetism of Multilayered Fe/AlN Prepared by Rf-sputter Deposition.
- コウシュウハ スパッタホウ ニヨル Fe AlN セキソウ マク ノ サクセイ
この論文をさがす
説明
Four kinds of Fe metal/A1N multilayered thin films were deposited by rf-sputter deposition at room temperature. Both Fe and AIN layers have almost the same thickness and their total film thikness was about 1u m. They have stacking sequences of 1, 3, 8 and 35 times, respectively. They showed an anisotropic magnetic behavior; soft ferromagnetic and mostly paramagnetic when a magnetic field was applied along and vertically against the film surface, respectively. Larger saturation magnetization in 10 to 20% than that of α-Fe was observed on the multilayers in the 3 and the 8 times stacking. Larger internal magnetic field component in about 10% than that of α-Fe was present in Mossbauer spectra for these films. Formation of both iron nitride and aluminum metal were detected at the interface of the multilayers by XAFS, Mössbauer spectrocopy and XPS even though the films were prepared at room temperature.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 43 (12), 1420-1425, 1996
一般社団法人 粉体粉末冶金協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206306804608
-
- NII論文ID
- 10002261178
-
- NII書誌ID
- AN00222724
-
- COI
- 1:CAS:528:DyaK2sXnsVaitA%3D%3D
-
- ISSN
- 18809014
- 05328799
- http://id.crossref.org/issn/05328799
-
- NDL書誌ID
- 4118677
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可