Products Obtained by Heating Cr Powder in CH4+NH3 Mixed Gas of Normal-Pressure
-
- Tanaka Kazuhiko
- Institute of Industrial Science, The University of Tokyo
-
- Hayashi Koji
- Institute of Industrial Science, The University of Tokyo
書誌事項
- タイトル別名
-
- Products Obtained by Heating Cr Powder in CH4+NH3 Mixed Gas of Normal-Psressure.
この論文をさがす
抄録
The synthesis of new mono-carbonitride powders of W and Mo, i.e., W(C, N) and Mo(C, N), have already been succeeded by authors by a normal-pressure method, i.e., heating metal powder in CH4+NH3 mixed gas of normal-pressure. In this study, the synthesis of mono-carbonitride of Cr in the same VIA group in the periodic table as W and Mo was attempted by the normal-pressure method. As the result, Cr(C, N) containing a small amount of Cr3C2 and Cr2N was obtained by heating of 1173 K-57.6ks. The nitrogen content (N/Cr)of Cr(C, N) in the product was estimated to be between about 40 and 60 at%. This value was considerably lower than 78-92 at% of pure Cr(C, N) synthesized by high-pressure method, i.e., heating metal+C mixed powder in N2 of 100-150MPa.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 49 (4), 279-283, 2002
一般社団法人 粉体粉末冶金協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206306817792
-
- NII論文ID
- 10008222539
-
- NII書誌ID
- AN00222724
-
- COI
- 1:CAS:528:DC%2BD38XjvVWqsb8%3D
-
- ISSN
- 18809014
- 05328799
- http://id.crossref.org/issn/05328799
-
- NDL書誌ID
- 6146160
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可