- タイトル別名
-
- On the Nitrided Layer of Sintered Cr-Steel
- ショウケツ Cr コウ ノ チッカソウ
この論文をさがす
説明
Sintered Cr-steels containing 1-3% Cr were prepared from the mixtures of iron powder, Cr3C2 powder and graphite powder, by compacting and sintering at 1250°C in vacuum. Specimens were nitrided at 500°C in an ammonia gas atmosphere, and the nitrided layer was examined. The results obtained are as follows:<BR>(1) Specimens containing more than 2%Cr give nearly same hardness distribution pattern after nitriding for 1 hr, compared with that of conventional Cr-steel nitrided for long time.<BR>(2) Rapid nitriding is due to the penetration of nitriding gas through pores of specimen, therefore nitrides are formed on the inner surface of pores and grain boundaries connecting with pores.<BR>(3) Although sintered specimens absorb large amounts of nitrogen, an X-ray diffraction pattern of the surface layers clearly shows a phase peak. This peak shifts to lower angle direction with an increase of Cr content, which shows lattice strain of a phase, and may contribute to the hardness increase.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 26 (3), 100-104, 1979
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206307031936
-
- NII論文ID
- 130000819935
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 2050511
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可