Preparation and Characterization of Solid Solutions of TiO2 and Trirutile Type MSb2O6 (M=Cu, Zn, Mg, Co and Ni)
-
- Katsui Akinori
- Dept. of Materials Chemistry, School of High-Technology for Human Welfare, Tokai University
-
- Hatano Ken
- Dept. of Materials Chemistry, School of High-Technology for Human Welfare, Tokai University
-
- Matsushita Hiroaki
- Dept. of Information and Communication Technology, School of High-Technology for Human Welfare, Tokai University
この論文をさがす
抄録
The solid solution of trirutile-type MSb2O6 (M=Cu, Zn, Mg, Co and Ni) and TiO2 with the molar rates x=0.125, 0.25, 0.5 and 0.75 in (MSb2O6)x(TiO2)1-x was prepared by a solid state reaction. The results showed that the solid solutions were formed except for (MSb2O6)0.75(TiO2)0.25 (M=Mg and Co) and x=0.50 and 0.75 in (NiSb2O6)x(TiO2)1-x, and were crystallized in trirutile type structure. Diffuse reflectance spectroscopy measurement for their powders indicated that the energy bandgaps were approximately 2.1 eV for (CoSb2O6)x(TiO2)1-x (x=0.125, 0.25 and 0.5), and were approximately 2.6 and 2.4 eV for (NiSb2O6)x(TiO2)1-x (x=0.125 and 0.25) and (CuSb2O6)x(TiO2)1-x (x=0.125, 0.25, 0.5 and 0.75), respectively. The photocatalytic activity for visible light was observed in (CoSb2O6)x(TiO2)1-x and (CuSb2O6)x(TiO2)1-x.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 54 (7), 479-483, 2007
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206307262592
-
- NII論文ID
- 130000057993
-
- NII書誌ID
- AN00222724
-
- COI
- 1:CAS:528:DC%2BD2sXot12is74%3D
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 8906097
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可