アルミナ板状粒子の粒成長に及ぼすMgO添加効果とその焼結体の機械的特性

書誌事項

タイトル別名
  • Effect of Addition of MgO on Platelike Grain Growth in Alumina Sintered Bodies and Their Mechanical Properties.
  • アルミナ イタジョウ リュウシ ノ リュウ セイチョウ ニ オヨボス MgO

この論文をさがす

抄録

Effect of addition of MgO on growth behavior of platelike grains in alumina sintered bodies was investigated and also their mechanical properties were investigated. The growth of platelike grains in the direction of long axis were restrained by addition of MgO, so the aspect ratio of the grains decreased with increasing amount of MgO. However, platelike grain growth mechanism with any amount of MgO up to 0.1mass% was considered to be similar, because the slopes of growth isotherms in log-log plot of platelike grain size of long axis versus sintering time were nearly equivalent. Although the bending strength of alumina sintered bodies with 20-30vol% platelike grains was almost. the same in comparison with the bodies which did not contain platelike grains, the fracture toughness of the former bodies were about 10-40% larger than the latter bodies. The mechanism of increasing fracture toughness in this study was considered to be the crack deflection process. The fracture toughness increased with aspect ratio of platelike grains in sintered bodies.

収録刊行物

被引用文献 (2)*注記

もっと見る

参考文献 (12)*注記

もっと見る

詳細情報 詳細情報について

問題の指摘

ページトップへ