- Crystal Stability and Magnetic Properties of W-type Hexagonal Ferrite Sr1-xBax(ZnLi0.5Fe0.5)Fe16O27.
- 6ポウショウ Wガタ フェライト Sr1-xBax ZnLi0.5Fe0.5
この論文をさがす
抄録
Crystal stability and possibility as an anisotropic permanent magnet of W-type hexagonal ferrite with composition of Sr1-xBax [ZnLi0.5Fe0.5]Fe16O27 was investigated. In this study, we found that the amount of Fe2+ in the calcined compound gradually increases with increasing Sr. In the ball-milled compound followed by annealing at 900-1100°C, W phase of Sr[ZnLi0.5Fe0.5]⋅Fe16O27 partially decomposed into M phase and spinel phase. On the other hand, Ba [ZnLi0.5Fe0.5]Fe16O27 remained a single phase. It can be assumed that Fe2+ substituted for (Li+0.5+Fe3+0.5) or Zn2+, and oxidation such as Fe2+→Fe3+ givies rise to decomposition.<BR>The grain size of Sr [ZnLi0.5Fe0.5]Fe16O27 and Ba [ZnLi0.5Fe0.5]Fe16O27 sintered at 1175-1225°C, respectively, was 0.3-5.0μm, their coercivity was less than 1000 Oe, and anisotropy energy (KA) and anisotropy field (HA) were estimated with about 60% of those of M-type ferrite. In conclusion, a preparation method of ferrite magnet hgaving more finer grains is necessitated for the practical use.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 43 (8), 995-1000, 1996
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206307681408
-
- NII論文ID
- 10002012819
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 4012523
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可