Sintering of PbO added (Pd, Ba) (Zn, Mg, Nb, Ti) O3 ceramics and their dielectric properties.

DOI Web Site 2 Citations

Bibliographic Information

Other Title
  • ＰｂＯを過剰に加えた（Ｐｂ，Ｂａ）（Ｚｎ，Ｍｇ，Ｎｂ，Ｔｉ）Ｏ３の焼結と誘電的性質
  • PbO オ カジョウ ニ クワエタ Pb Ba Zn Mg Nb Ti O3

Search this article

Abstract

The powder of (Pb, Ba) (Zn, Mg, Nb, Ti)O3 system ceramics developed as the multilayer capacitor material with the optimum firing temperature of 1100°C was mixed with small amount of excess PbO as a sintering aid and ground to submicron by ball-milling using the partially stabilized zirconia balls of 3 mmφ. Microstructures such as density, grain size or liquidus phase of the ceramics fabricated from the powders were examined as a function of excess PbO content by SEM and DTA. Densification was enhanced by addition of excess PbO at the firing temperature lower than 1000°C, and the dense ceramic bodies above 7.7 g/cm3 with small grain were obtained at firing temperature of 750°C. Temperature dependence of dielectric constants were measured by a LF inpedance analyzer at 1 kHz. For the 2 mol%PbO added ceramics sintered at 800°C, relative permittivity at room temperature higher than 10000 was successfully attained without remarkable change of loss factor and insulation resistance from those of the stoichiometric ceramics sintered at 1100°C.

Journal

Citations (2)*help

See more

Keywords

Details 詳細情報について

Report a problem

Back to top