Production of Amorphous Soft Magnetic Powders by the New Water Atomization Process "SWAP".

DOI Web Site 5 Citations 13 References Open Access

Bibliographic Information

Other Title
  • 新しい水アトマイズ法（ＳＷＡＰ法）によるアモルファス軟磁性粉末の作製
  • アタラシイ ミズ アトマイズホウ SWAPホウ ニ ヨル アモルファス ナンジセイ フンマツ ノ サクセイ

Search this article

Description

In this paper, characteristics of the amorphous soft-magnetic alloy powders fabricated by the new atomization process "SWAP; Spinning Water Atomization Process" with both of high quenching rate and possibility of the mass-production are presented.<BR>In the equipment, gas-atomized droplets are rapidly quenched by the effect of centrifugal force of the high speed spinning water. The speed, the depth and the temperature of the spinning water influence the quenching rate of droplets. Fe-Si-B alloy powders produced by this method were in the amorphous state at particle size up to 300μm in diameter and exhibited good soft-magnetic properties and very low oxygen contents of about 100-200ppm. The powder surface observed by SEM was smooth and their morphology was spherical for finer particle and rather flat for larger particle, suitable for forming consolidated powder core. Therefore, "SWAP" is expected to be useful for high production yield of amorphous powder and to be available for development of amorphous powder cores.

Journal

Citations (5)*help

See more

References(13)*help

See more

Keywords

Details 詳細情報について

Report a problem

Back to top