- Effects of the Additives on Sintering of Si<SUB> 3</SUB>N<SUB> 4</SUB>
- チッカ ケイソ ノ ショウケツ ニ オヨボス カクシュ テンカザイ ノ コウカ
この論文をさがす
説明
Effects of the additives on sintering of Si 3N4 have been studied. As the additives, Al(OH) 3, Al powder, A1PO4, AIN, SiC, Si powder, SiO2, MgO, TiO2, BN, Fe2O3, etc. were used. The powder of Si 3N 4 was mixed with 1, 3 or 5 wt. % of the additive, and then was pressed isostatically at 1000 kg/cm2. Sintering was done in the N 2 atmosphere at 1530°C for 4 hours. The most effective additive was MgO at 5 wt. %, followed by MgO at 3 wt. %, and the third was Al(OH) 3 at 5 wt. %. Moduli of rupture of these bodies were 830 kg/cm2, 664 kg/cm2, and 414 kg/cm2 respectively.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 13 (4), 186-191, 1966
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206307984640
-
- NII論文ID
- 130000817543
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 8444151
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可