- Slip casting and sintering of high purity alumina.
- コウ ジュンド アルミナ ノ スリップ キャスティング セイケイ ト ソノ シ
この論文をさがす
説明
Slip casting method for submicron high purity alumina was developed by optimizing the concentration of slip and dispersant, and using resin mold as a substitute for plaster and apparatus with vacuum⋅pressure system. The results obtained were summarized follows:<BR>1) High density green body (>60%) was obtained.<BR>2) High strength alumina (700-800MPa) was obtained after sintering the body at 1250-1300°C. This value is equal to that of alumina sintered under HIP and HP at 1500-1600°C.<BR>3) This high strength comes from uniformally controlled small grain size(1-3μm) of sintered body which results in grain fracturing instead of grain boundary fracturing of conventional alumina ceramics.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 35 (7), 619-624, 1988
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206308038656
-
- NII論文ID
- 130000813415
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 3210062
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDLサーチ
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可