- Effect of Addition of a Small Amount of Zr on the Sintering behavior of Water Atomized 316L Stainless Steel Powder
- ミズ アトマイズホウ デ サクセイ シタ ビリョウ Zr テンカ ゴウキンフンマツ ノ ショウケツ トクセイ
この論文をさがす
説明
The main objective of the present work is to evaluate the effects of Zr addition on various properties of SUS316L stainless steel powders produced by water-atomization of liquid metals. The results are summarized as follows;<BR>1) The sintering density of SUS316L stainless steel powders pre-alloyed with 0.05 mass% of Zr was about 2 percent higher than that of the powder containing no Zr. However, in the powder pre-mixed with 0.05 mass% of Zr, no effect of Zr addition was observed.<BR>2) Mechanical properties were improved by pre-alloying with Zr, but impaired by pre-alloying with Zr.<BR>3) In pre-alloyed powder with 0.05 mass% of Zr, the increase of sintering density to start from 1073 K was observed. The micro-structural observation showed that the neck formation between particles started at 1073 K. The temperature is lower by about 100 K compared with the powder containing no Zr.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 57 (2), 126-133, 2010
一般社団法人 粉体粉末冶金協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206308094592
-
- NII論文ID
- 10026346313
-
- NII書誌ID
- AN00222724
-
- COI
- 1:CAS:528:DC%2BC3cXjtVOnt7w%3D
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 10583736
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDLサーチ
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可