- Quantitative Analysis of Microstructure Development during Sintering of High Purity Alumina Made by High-Speed Centrifugal Compaction process.
- コウソク エンシン セイケイホウ ニ ヨル コウジュンド アルミナ ノ ショウ
この論文をさがす
抄録
An overall development of microstructure during sintering of high purity sub-micron alumina is investigated. The alumina is compacted by the High-Speed Centrifugal Compaction Process (HCP alumina). An alumina powder with a purity of 99.99 mass% and mean particle size of 0.22μm is dispersed in 25 mass% of ion-exchanged water, compacted applying a centrifugal force of 10, 000-20, 000 g for 3 ks, and sintered at 1473-1623 K for 0-172.8 ks in air.<BR>The microstructure of sintered HCP alumina has particular combination of its density and grain size in each sintering condition, and they make single grain-size/relative-density trajectory. The location of the trajectory shifts toward smaller in grain size and higher in density compared to previously reported ones.<BR>The grain-size/relative-density trajectory is divided into three stages as the microstructure morphology changes. In the stage I, the microstructure is composed of open pore network, and its trajectory shows a straight line with low gradient. In the stage II, the microstructure has closed pores and the trajectory curves upward. After the density almost reaches uppermost limit, the morphological development enters to stage III, and steep straight trajectory is observed.<BR>The sintered compact at the boundary of stage II and III shows the highest strength. The microstructure of that body has a density of about 99 % and homogeneous fine grains with equi axed isolated pores located at the four-grain corners.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 45 (12), 1122-1130, 1998
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206308189440
-
- NII論文ID
- 10002053345
-
- NII書誌ID
- AN00222724
-
- COI
- 1:CAS:528:DyaK1MXltVajsQ%3D%3D
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 4629446
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可