Structures and Mechanical Properties of Ti-37.5at%Si Compacts Prepared by High Hydrostatic Pressure Consolidation Using Mechanically Alloyed Powders.
-
- Matsumoto Akihiro
- National Industrial Research Institute of Nagoya
-
- Kobayashi Keizo
- National Industrial Research Institute of Nagoya
-
- Takagi Makoto
- Aichi Institute of Technology
-
- Imura Toru
- Aichi Institute of Technology
Bibliographic Information
- Other Title
-
- MA‐超高圧成形により作製したTi‐37.5at%Siバルク体の組織と機械的特性
- MA-チョウコウアツ セイケイ ニ ヨリ サクセイ シタ Ti-37.5atパ
Search this article
Abstract
Ti-37.5at%Si powder mixtures were mechanically alloyed in a-planetary ball mill under an Ar atmosphere. The powder prepared by milling for 50 hr, consisted of amorphous and nano-sized Si grains, was consolidated using a cubic type anvil apparatus under a high hydrostatic pressure of 5.4GPa. The compact consolidated at 623K was fully densified with the retention of non-equilibrium structures. The compressive strength of the compact at room temperature was about 2.5GPa.
Journal
-
- Journal of the Japan Society of Powder and Powder Metallurgy
-
Journal of the Japan Society of Powder and Powder Metallurgy 45 (12), 1211-1215, 1998
Japan Society of Powder and Powder Metallurgy
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390001206308224256
-
- NII Article ID
- 10002053527
-
- NII Book ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL BIB ID
- 4629461
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed