- Mg-Si Film Deposition on Magnesium Alloy and Its Characteristics by Employing Mg2Si Sintered Material
- Mg2Si焼結体を用いたマグネシウム合金へのMg-Si成膜プロセスと皮膜特性
- Mg2Si ショウケツタイ オ モチイタ マグネシウム ゴウキン エ ノ Mg Siセイマク プロセス ト ヒマク トクセイ
この論文をさがす
抄録
Coating technology by using magnesium silicide intermetallics (Mg2Si) was developed to improve the surface properties of magnesium alloys. This is because they have superior corrosion resistance to the conventional stainless steel and high Young's modulus and hardness. In this study, Mg-Si thin film deposited on AZ31 magnesium alloys by using a high frequency sputtering method was examined when employing the sintered Mg2Si bulky materials as sputtering targets. The change in the sputtering Ar gas pressure enables the structure control of Mg-Si thin film; crystal structures at lower pressure and amorphous one over 4 Pa. Some results of SST to evaluate the corrosion resistance indicated that AZ31 substrate with Mg-Si coating showed no damage after 240 h. On the other hand, that with no coating was corroded within only 1 h, and showed remarkably damaged surfaces. Pin on disk type wear test under oil lubricant indicated that a friction coefficient, μ was low and stable in using AZ31 alloy disk specimen coated by Mg-Si film. The disk specimen with no coating showed severely damaged surface including seizure or sticking phenomena with S35C pin specimens. In particular, the amorphous Mg-Si film showed superior anti-seizure properties to the crystalline one because of higher hardness and Young's modulus.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 52 (4), 276-281, 2005
一般社団法人 粉体粉末冶金協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206308273792
-
- NII論文ID
- 130000055958
- 30021673721
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 7331637
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可