- Sintering of Cr1-xMoxB2 Ceramics.
- Cr1-xMoxB2ケイ セラミックス ノ ショウケツ
この論文をさがす
抄録
Cr1-xMoxB2 ceramics were manufactured by hot-pressing at the temperatures between 1600 and 1900°C. CrB2, Mo and amorphous boron powders were mixed in selected ratios. The ceramics were characterized by lattice constants, density and hardness.<BR>The X-ray diffraction data showed that the molybdenum solubility x into the ceramics is about 0.6 at the temperatures of 1600-1800°C and increases to about 0.8 at 1900°C. Apparent density of the ceramics increased as molybdenum content and hot-pressing temperature increased. SEM observations showed that boride grains in the ceramics grows rapidly over the hot-pressing temperature of 1800 °C . Vickers hardness of the ceramics is a function of hot-pressing temperature and molybdenum content, and reached maximum value of 26.5GPa at 1700°C and x=0.6.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 44 (3), 222-226, 1997
一般社団法人 粉体粉末冶金協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206308536064
-
- NII論文ID
- 10002013580
-
- NII書誌ID
- AN00222724
-
- COI
- 1:CAS:528:DyaK2sXisVCktbw%3D
-
- ISSN
- 18809014
- 05328799
- http://id.crossref.org/issn/05328799
-
- NDL書誌ID
- 4172703
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可