- Interdiffusion in Iron Powder and Nonferrons Metal Powder System under Hot-pressing
- ホット プレス ニヨル テツ アップンタイ ヒテツ キンゾク アップンタイカン
この論文をさがす
抄録
Interdiffusion in iron compact and nickel, cobalt, chromium, molybdenum or tungsten compact system under hot-pressing has been investigated and the results obtained are as follows. Width of diffusion band between the compacts increases as hot-pressing temperature increases in any system. The systems can be classified into the following two groups based on the rate of width-increase. One is the iron-nickel and the iron-cobalt systems in which the width of diffusion band is large under hot-pressing at 1000°C-1200°C, but small under hot-pressing at 1300°C-1400°C as compared with other systems. The other is the iron-chromium, the iron-molybdenum and the iron-tungsten systems in which the width of diffusion band is small under hot-pressing at 1200°C, but remarkably large under hot-pressing temperature at 1300°C-1400°C because intermetallic compounds generate as diffusion proceeds.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 24 (6), 175-182, 1977
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206308595456
-
- NII論文ID
- 130000818566
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 1846120
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可