- Effect of SiO2-SrCO3 Addition on Magnetic Properties of Anisotropic Ba-ferrite(Ferrite Magnets Having Equal Shrinkage Ratio in A-axis and C-axis).
- イホウセイ Ba フェライト ニ タイスル SiO2 SrCO3 フクゴウ テ
この論文をさがす
説明
Today, Sr-ferrite and Ba-ferrite with hexagonal structure are widely used as permanent magnets. However, Ba-ferrite is considered to be unsuitable for high performance magnets compared with Srferrite because of its lower K1 value. In this study, submicron-sized Ba-ferrite powders were prepared to achieve higher corecivity. On the other hand, addition of SiO2 and CaCO3 (or CaO) is usually carried out to get high density and inhibit grain-growth during sintering. Without difficulty, it is predicted that Sr and Ba can be substituted for Ca, because they have similar characters. Therefore, in this study, addition of alkaline-earth elements and silica was investigated systematically. As a result, by addition of Si02-SrCO3 in Ba-ferrite, high performance Ba-ferrite magnets (Br=4.3kG, HcJ=3.6kOe) were obtained. At the same time, we discovered that they have equal shrinkage ratio in a-axis and c-axis. These unique results were due to the inhibition of grain-growth along a-axis. Furthermore, Ba segregation was found at grain boundaries besides Si and Sr by TEM-EDS analysis.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 43 (1), 19-24, 1996
一般社団法人 粉体粉末冶金協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206308789248
-
- NII論文ID
- 10002010991
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 3918028
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDLサーチ
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可