- The friction and wear properties of ceramics - The effects of metal deposition and ion irradiation.
- セラミックス ノ マサツ マモウ トクセイ キンゾク ハクマク ノ ジョウチャ
- The Effects of Metal Deposition and Ion Irradiation
- 金属簿膜の蒸着とイオン照射の効果
この論文をさがす
抄録
SiC ceramics, the one deposited with niobium metal film (Nb/SiC) and Ar+ ion-irradiated Nb/SiC were subjected to a pin-on-disk friction and wear test in an ambient atmosphere with a diamond pin for 40 hours. The friction coefficient between SiC and diamond pin was about 0.1. The Nb film deposition reduced the friction coefficient and it was about 0.04 with the normal load of 1000 gf. The wear of SiC was also reduced to one seventh by the Nb deposition. The Ar+ ion-irradiated Nb/SiC was found to have very high wear resistivity and effectively no wear was detected in the samples irradiated to the doses over 5×1015 ions/cm2.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 35 (3), 174-176, 1988
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206309026304
-
- NII論文ID
- 130000813257
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 3184638
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可