Magnetic Properties of High Coercivity Melt-Spun Didymium-Fe-Co-Nb-V-Y-Hf-B System Ribbons and Their Bonded Magnets
-
- Yamamoto Hiroshi
- School of Science and Technology, Meiji University
-
- Sato Tomonori
- School of Science and Technology, Meiji University
Bibliographic Information
- Other Title
-
- 高保磁力Didymium‐Fe‐Co‐Nb‐V‐Y‐Hf‐B系急冷薄帯並びにそれらボンド磁石の磁気特性
- 高保磁力Didymium-Fe-Co-Nb-V-Y-Hf-B系急冷薄帯並びにそれらボンド磁石の磁気特性
- コウホジリョク Didymium Fe Co Nb V Y Hf Bケイ キュウレイ ハクタイ ナラビニ ソレラ ボンド ジシャク ノ ジキ トクセイ
Search this article
Abstract
The melt-spun ribbons of Didymium-Fe-Co-Nb-V-Y-Hf-B system alloys were prepared by single roller liquid rapid-quenching method, and the effects of composition, wheel velocity and heat treatment on the magnetic properties were investigated. As the result, Didymium11.0Fe69.6Co10Nb1V1Y0.7Hf0.7B6 optimum composition ribbons prepared at a wheel velocity of 22.5 m/s were crystallized by heat treatment, and the optimum heat treatment condition was found to be at 725°C for 5 min, and then the values of (BH)max and HcJ were 105.7 kJ/m3, 1307.4 kA/m, respectively. The temperature coefficients of Jr and HcJ for the ribbons crystallized from the melt-spun Didymium11.0Fe69.6Co10Nb1V1Y0.7Hf0.7B6 alloy were α(Jr)ave.=−0.10 %/°C (reversible) and α(HcJ)=−0.48 %/°C (irreversible), respectively. The value of (BH)max for the isotropic compression molding Didymium11.0Fe69.6Co10Nb1V1Y0.7Hf0.7B6 bonded magnet prepared by using the ribbons annealed at 725°C for 5 min is 56.6 kJ/m3 and the density is 6.14 Mg/m3. Irreversible loss of the isotropic bonded magnet are −1.21% (at 150°C) and −2.42% (at 200°C).
Journal
-
- Journal of the Japan Society of Powder and Powder Metallurgy
-
Journal of the Japan Society of Powder and Powder Metallurgy 55 (7), 529-534, 2008
Japan Society of Powder and Powder Metallurgy
- Tweet
Details 詳細情報について
-
- CRID
- 1390001206309037440
-
- NII Article ID
- 10024350657
-
- NII Book ID
- AN00222724
-
- COI
- 1:CAS:528:DC%2BD1cXovFehtbo%3D
-
- ISSN
- 18809014
- 05328799
-
- NDL BIB ID
- 9587197
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed