Ｂｉ２Ｏ３‐ＣｕＯ系Ｂｉ２ＣｕＯ４についての考察

池田 靖訓, 佐野 恭司, 坂東 尚周, 新苗 稔展, 高田 潤

doi:10.2497/jjspm.41.384

書誌事項

タイトル別名

Consideration of Bi2CuO4 in the Bi2O3-CuO System.
Bi2O3 CuOケイ Bi2CuO4 ニツイテノコウサツ

この論文をさがす

説明

The composition around Bi₂CuO₄ in the Bi₂O₃-CuO system was studied using DTA and X-ray analysis. Only the compound Bi₂CuO₄ was confirmed in the Bi₂O₃-CuO system as reported previously. The eutectic temperature was observed between 750°C to 760°C, which is 10°C to 20°C lower than the value previously reported. The monoclinic (α-form) to cubic (δ-form) transition of Bi₂O₃ was observed at 730°C, which is in good agreement with the previous studies.<BR>The interesting crystallization of γ-Bi₂O₃ was observed in the narrow composition range about 60-50 mol % Bi₂O₃ when it was quenched above 760°C in air. However, α-Bi₂O₃ was observed in the more Bi₂O₃ rich composition at 70 mol % B1₂0₃.

収録刊行物

粉体および粉末冶金

粉体および粉末冶金 41 (4), 384-387, 1994

一般社団法人粉体粉末冶金協会

キーワード

詳細情報詳細情報について

CRID: 1390001206309047296

NII論文ID: 130000819527

NII書誌ID: AN00222724

DOI: 10.2497/jjspm.41.384

ISSN: 18809014; 05328799

NDL書誌ID: 3878301

Web Site: http://id.ndl.go.jp/bib/3878301; https://ndlsearch.ndl.go.jp/books/R000000004-I3878301

本文言語コード: ja

データソース種別

JaLC
NDLサーチ
Crossref
CiNii Articles
OpenAIRE

抄録ライセンスフラグ: 使用不可

書き出し

問題の指摘