Magnetic Properties of Crystal Oriented Ni-Zn Ferrites for High Frequency.

DOI Web Site 9 References

Bibliographic Information

Other Title
  • 磁性材料　　配向性Ｎｉ‐Ｚｎフェライトの高周波磁気特性
  • ハイコウセイ Ni Zn フェライト ノ コウシュウハ ジキ トクセイ

Search this article

Description

Acicular Ni0.4Zn0.6Fe2O4 fine particles were made from acicular a-FeOOH, Ni(C5H7O2)2 and Zn(C5H7O2)2 by calcining at 750-950°C for 4 hours. The saturation magnetization and the aspect ratio of the obtained particles were 50 emu/g and 26, respectively. These particles were pressed in a die into a troidal shape. In the pressing process, they were grain-oriented by multi-layer formation or magnetic field application so that their <111> direction in the spinel structure could be aligned perpendicular to the top surface of the troidal core. In addition, the randomly oriented sample was also prepared as a reference. These pressed compacts were sintered at 1200-1300°C for 6h. The initial permeability of the grain-oriented samples were larger than that of the randomly oriented sample. Moreover, the frequency dependence of reflection loss in these grain-oriented samples were improved.

Journal

References(9)*help

See more

Keywords

Details 詳細情報について

Report a problem

Back to top