Characterization and Sintering of LaAlO3 Powder Prepared by the Hydrazine Method.
-
- Hirota Ken
- Department of Molcular Science and Technology, Faculty fo Engineering, Doshisha University
-
- Iketani Kazuya
- Department of Molcular Science and Technology, Faculty fo Engineering, Doshisha University
-
- Yoshinaka Masaru
- Department of Molcular Science and Technology, Faculty fo Engineering, Doshisha University
-
- Yamaguchi Osamu
- Department of Molcular Science and Technology, Faculty fo Engineering, Doshisha University
この論文をさがす
抄録
Lanthanum aluminum oxide LaAlO3 is formed at low temperatures (-870°C) from an amorphous material prepared by the hydrazine method. Powder characterization has been conducted using XRD, DTAITG, TEM, and BET method; LaAlO3 powders heated at 900°-1500°Crevealed that they consisted of submicrometer-sized translucent particles. They were sintered at 1800°C for 2h in air, dense ceramics with a 96.4% of theoretical have been obtained from the powder calcined at 1200°C. They exhibit the microstructure composed of well-developed grains (-140μm) with intergranular and intragranular pores of-13 and-7μm, respectively. Electric property has been evaluated; their dielectric constant at room temperature is 36.5±1.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 49 (7), 576-580, 2002
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206309129472
-
- NII論文ID
- 10009579568
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 6227680
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可