- Influences of Pulverized Particle Size and Magnetic Field during Compacting on the Degree of Alignment of Sr-Ferrite.
- Sr フェライト ノ ハイコウド ニ オヨボス フンサイ リュウド ト セイケ
この論文をさがす
抄録
Influences of pulverized particle size (0.67, 0.95, 1.14 and 1.39, μm) and magnetic field (0, 239, 478, 716 and 915kA/m) during compacting on the degree of alignment of Sr-ferrite were investigated using X-ray pole figure. Degrees of alignment of the compacted green bodies with average particle sizes of 0.95, 1.14 and 1.39 μm are saturated in a magnetic field of 239kA/m parallel to the compacting direction. To the contrary, applying the magnetic field perpendicular to the compacting direction, they are saturated in a magnetic field of 478kA/m. In the magnetic field lower than 478kA/m, degrees of alignment of the parallel configuration are higher than those of the perpendicular configuration, which is independent of particle size. In particular, at a small particle size of 0.67 μm, degree of alignment of the parallel configuration tends to be higher than that of the perpendicular configuration under any applied field.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 45 (1), 77-81, 1998
一般社団法人 粉体粉末冶金協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206309173504
-
- NII論文ID
- 10003382193
- 10002014956
-
- NII書誌ID
- AN00222724
-
- COI
- 1:CAS:528:DyaK1cXhtFOgsL8%3D
-
- ISSN
- 18809014
- 05328799
- http://id.crossref.org/issn/05328799
-
- NDL書誌ID
- 4392669
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可