- Consolidation of mechanically milled powder mixture of aluminum and quasicrystalline particle.
- メカニカルミリング シタ ジュンケッショウ リュウシ アルミニウム ゴウキンフ
この論文をさがす
抄録
A quasi-crystalline Al65Cu20Fe15 powder prepared from alloy cast rapidly solidified by metal-mold casting, and then it was mixed to aluminum powder with various volume fractions by mechanical milling. The powder milled for above 50ks made homogeneous dispersion of quasi-crystalline phase with particle size less than 1μm. The powder was hot-pressed under various conditions and then its features of consolidation were examined by the observation of microstructure and fracture strength in 3-point-bending of the compacts. When the milled powder was hot-pressed at higher compacting temperature than 673K for 3.6ks under pressure of 600MPa, the compact became to dense. Hardness of the obtained compact increases and its fracture strength decreases with increasing volume fraction of quasi-crystalline particles. Intermetallic compound Al7Cu2Fe forms in the interface of aluminum matrix and quasi-crystalline particle.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 45 (10), 995-999, 1998
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206309186048
-
- NII論文ID
- 10002053091
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 4585469
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可