Ｎｉ焼結多孔体の界面インピーダンス法による比表面積への焼結雰囲気の影響

DOI Web Site 参考文献6件

書誌事項

タイトル別名
  • Effect of Sintering Environment on Specific Surface Area of Sintered Porous Ni Compact Measured by Interfacial Impedance Method.
  • Ni ショウケツ タコウタイ ノ カイメン インピーダンスホウ ニ ヨル ヒ

この論文をさがす

抄録

The sintered porous Ni is very important as electrode materials and have been used widely. In this work, the effect of the sintering environments and characteristics of raw Ni powders of the three kinds on the specific surface area of the sintered porous Ni compact was investigated. They were sintered at 1173K and 1273K for 1 hour under the both sintering environments, capsule free HIP (CFHIP) of 120MPa of argon gas and vacuum. The specific surface area was measured by interfacial impedance method.. The specific surface area of the sintered porous compact formed from the smallest particle size Ni was the largest under the both sintering environments, CFHIP and vacuum, and at the each sintering temperature. The specific surface area of the porous Ni compact sintered in CFHIP was larger than in vacuum for every raw Ni powder.

収録刊行物

参考文献 (6)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ