- Effect of Sintering Environment on Specific Surface Area of Sintered Porous Ni Compact Measured by Interfacial Impedance Method.
- Ni ショウケツ タコウタイ ノ カイメン インピーダンスホウ ニ ヨル ヒ
この論文をさがす
説明
The sintered porous Ni is very important as electrode materials and have been used widely. In this work, the effect of the sintering environments and characteristics of raw Ni powders of the three kinds on the specific surface area of the sintered porous Ni compact was investigated. They were sintered at 1173K and 1273K for 1 hour under the both sintering environments, capsule free HIP (CFHIP) of 120MPa of argon gas and vacuum. The specific surface area was measured by interfacial impedance method.. The specific surface area of the sintered porous compact formed from the smallest particle size Ni was the largest under the both sintering environments, CFHIP and vacuum, and at the each sintering temperature. The specific surface area of the porous Ni compact sintered in CFHIP was larger than in vacuum for every raw Ni powder.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 45 (9), 796-800, 1998
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206309273856
-
- NII論文ID
- 10002052706
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 4566299
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可