- Preparation of porous carbon composite with highly dispersed ultra fine metal compound from metal ion exchanged resin-Hardness and magnetic properties.
- イオン コウカン ジュシ カラ ノ チョウビリュウシ キンゾク カゴウブツ コ
- Hardness and magnetic properties
- 硬度及び磁気特性
この論文をさがす
抄録
Porous carbon composites with highly dispersed ultrafine metal compounds (carbide, or nitride of Fe, Mo, W) were prepared by carbothermal reduction from metal ion exchanged resin. All the carbonized samples maintained their original spherical shape but their diameters shrunk to 60-80% of their initial sizes. Metal compounds in the carbonized sample were dispersed in the carbon matrix, and their particle diameters were 2-30nm. Some of the carbonized samples displayed a week needle trace or the trace gradually diminished within one minute during the vickers hardness measurement suggesting that the composite had elasticity. All the composites prepared from Fe 3+ adsorbed chelate resin showed strong magnetic properties. Residual magnetization was confirmed only in the carbonized sample which was prepared by heating to 800°C in N2 and cooled rapidly.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 45 (9), 806-811, 1998
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206309275648
-
- NII論文ID
- 10002052725
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 4566301
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可