- Synthesis of TiB2-TiN Composites by Reactive Spark Plasma Sintering of BN and Ti.
- BN ト Tiノ ハンノウセイ ホウデン プラズマ ショウケツ ニ ヨル TiB2 TiN フクゴウタイ ノ ゴウセイ
この論文をさがす
抄録
Reactive spark plasma sintering technique was applied to the synthesis of TiB2-TiNx composites from BN and Ti powders and the simultaneous consolidation of them. The nonstoichiometry of synthesized TiNx (x=0.6-1.0) was controlled by the change of the molar ratio of BN and Ti starting<BR>powders and the resulting displacement reaction 2BN+(1+2/x)Ti→(TiB2+2/xTiNx. When x is 0.9 and below, the relative density of composites reached more than 99.6 % at a sintering temperature of 2000°C, because of the good sinterability of nonstoichiometric TiNx. For dense composites, Young's<BR>modulus increased with x, but hardness decreased. The composite at x=0.9 had the highest values for Young's modulus (476 GPa) and fracture toughness (3.2 MPa m1/2)as well as good sinterability.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 46 (4), 383-389, 1999
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206309292288
-
- NII論文ID
- 10002262281
-
- NII書誌ID
- AN00222724
-
- COI
- 1:CAS:528:DyaK1MXkt1KltrY%3D
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 4701549
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可