- Magnetic Properties of Anisotropic Bonded Magnets Using Sr-La-Co System M-Type Ferrite Powders Prepared by Mechanical Compounding Method
- メカニカル コンパウンディングホウ ニ ヨリ サクセイ シタ Sr La Co ケイ Mガタ フェライト フンマツ オ モチイタ イホウセイ ボンド ジシャク ノ ジキ トクセイ
この論文をさがす
抄録
Sr-La-Co M-type ferrite powders were prepared by the mechanical compounding method using the planetary ball-mill and subsequent heat treatment. This experiment was carried out to investigate magnetic properties of bonded magnet using M-type ferrite powders prepared by Mechanical compounding method. The properties and making condition of typical sample are as follows; Chemical composition: SrO⋅6.3Fe2O3 in addition with 2.0 wt% La2O3 and 0.3 wt% Co3O4; planetary ball-mill condition: 300 rpm × 1 h; heat treatment condition: 1200°C×4h in air; centrifugal mill time: 1 h; binder: Nylon6 (ejection molding); magnetic properties are Jr= 0.252T; HcJ=307kA/m; (BH)max=12.3 kJ/m3 and density: 3.57 Mg/m3.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 50 (6), 444-447, 2003
一般社団法人 粉体粉末冶金協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206309326464
-
- NII論文ID
- 10011242278
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 6624844
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可