常圧及び加圧焼結のメカニズムとニヤネットシェイプ制御　高強度Ａｌ‐ＴＭ‐Ｌｎ系急冷凝固粉末の成形固化および材料特性

DOI Web Site 被引用文献1件 参考文献5件 オープンアクセス

書誌事項

タイトル別名
  • Consolidation and Mechanical Properties of High Strength Rapidly Solidified Al-TM-Ln Alloy Powder.
  • コウ キョウド Al TM Lnケイ キュウレイ ギョウコ フンマツ ノ セイ

この論文をさがす

説明

Rapidly solidified AI-TM-Ln base alloy has excellent mechanical properties such as high specific strength or specific modulus. In this study, Al92Ni4.5Ti1.5CulZr0.8Ce0.2 (at%) alloy powders were directly forged using a double action forging press without preparing a compact preform that is difficult to consolidate because of the spherical shape and hardness of the powder. The tensile strength of above test pieces preheated at 723K for 3600s shows 670MPa and 2% elongation, which is comparable with the test pieces prepared by extrusion from the same powder. This process gives near net shape parts with excellent mechanical properties using the rapidly solidified Al-TM-Ln base alloy.