- Crystal Orientation and Magnetic Properties of Mn-Zn Ferrites Made Use of Acicular .ALPHA.-FeOOH.
- シンジョウ アルファーFeOOH オ モチイタ Mn-Zn フェライト ノ ハイコウセイ オヨビ ジキ トクセイ
この論文をさがす
説明
Crystal oriented manganese zinc ferrites were made from acicular α-FeOOH, Mn(C5H7O2)3 and Zn(C5H7O2)2 as raw materials. The materials were mixed and calcined at 800°C for 4 hours in nitrogen atmosphere. The calcined acicular manganese zinc ferrite fine particles were formed into a thin troidal cores, consist of multi-layered. The green bodies were sintered at the range of 1100 to 1250°C for 4 to 8 hours in air, thereafter cooled in nitrogen atmosphere.<BR>The crystals of sintered manganese zinc ferrites were strongly oriented to the direction of {111} plane of the spinel, which was all formed along the upper plane of troidal cores. The behavior of crystal growth was similar to that of manganese zinc ferrite single crystal. The initial permeability of crystal oriented manganese zinc ferrites was 1380 at 0.1MHz and it was not allowed to decay up to 2.2 MHz at the operating condition of the 3dB decrease of the initial permeability. The high crystal orientation and suitable grain size has greatly contributed to the improvement of magnetic properties.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 46 (6), 621-625, 1999
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206309433216
-
- NII論文ID
- 10005139599
- 20000363512
-
- NII書誌ID
- AN00222724
-
- COI
- 1:CAS:528:DyaK1MXksFart7c%3D
-
- ISSN
- 18809014
- 05328799
- http://id.crossref.org/issn/05328799
-
- NDL書誌ID
- 4770236
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可