Corrosion Behavior of Ti-Mo Sintered Alloy.
-
- Nakahara Kenji
- Nippon Tungsten Co., Ltd.
-
- Tokumoto Kei
- Nippon Tungsten Co., Ltd.
-
- Sakaguchi Shigeya
- Nippon Tungsten Co., Ltd.
-
- Hayashi Yasunori
- Dept. Materials Science and Engineering, Fac. Eng. Kyushu University
Bibliographic Information
- Other Title
-
- Ti‐Mo系焼結合金の腐食挙動について
- Ti Moケイ ショウケツ ゴウキン ノ フショク キョドウ ニ ツイテ
Search this article
Abstract
The corrosion behavior of Ti-(0-40)mass%Mo alloys prepared through P/M technology was studied by corrosion test and electrochemical measurements. The corrosion rate of sintered Ti-Mo alloys in 35% HCl solution decreased remarkably with increasing molybdenum content. The corrosion rate of Ti-40mass%Mo alloy, for example, exhibited 5*10-3 [mm/year], which was 104 times lower than that of pure titanium. On the other hand, the corrosion rate in 3%NaCl solution wasn't affected by molybdenum content in alloys and was less than 10-3 [mm/Year].<BR>Potentiodynamic polarization curves in 35%HCl solution showed that increasing molybdenum content caused the open circuit potential (corrosion potential) to be noble and the anodic current density to be low. It was thought that the presence of spontaneously passivated film in which molybdenum was enriched by preferential dissolution of titanium suppressed the anodic reaction and improved their corrosion resistance. On the other hand, potentiodynamic polarization curves in 3%NaCl solution revealed that increasing molybdenum content caused the open circuit potential to be base and the anodic current density to be high because molybdenum dissolved actively.
Journal
-
- Journal of the Japan Society of Powder and Powder Metallurgy
-
Journal of the Japan Society of Powder and Powder Metallurgy 44 (3), 241-246, 1997
Japan Society of Powder and Powder Metallurgy
- Tweet
Details 詳細情報について
-
- CRID
- 1390001206309472384
-
- NII Article ID
- 10002013628
-
- NII Book ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL BIB ID
- 4172707
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed