Silicon nitride nanopowder was fabricated from a silicon nitride sub-micrometer powder by high energy milling. The sub-micrometer Si3N4 powder, 2 mol% of Al2O3 and 5 mol% of Y2O3 are mixed and then high-energy milled with Si3N4 balls as milling media in a Si3N4–lined pot filled with N2. Silicon nitride nanopowder with about 20 nm in diameter was obtained by high-energy milling at 475 rpm for 4 hs. Phase identification by XRD and TEM observation showed that the high-energy milled powder consisted of nanopowder with glassy phase. Effect of metallic aluminum was invesigated as a grinding additive. The addition of metallic aluminum enhanced the high-energy milling. These results suggest that nanopowder can be prepared by grinding method.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 60 (10), 420-427, 2013
一般社団法人 粉体粉末冶金協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206310298624
-
- NII論文ID
- 130003384135
-
- NII書誌ID
- AN00222724
-
- COI
- 1:CAS:528:DC%2BC3sXhvVWktb7E
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 024958440
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可